Special Coating Liquid Silicone Rubber Iota M1740 for Airbag, Architectural Textile, Protective Clothing
Special coating liquid silicone rubber for airbag IOTA M1740DescriptionM1740 A/B is a special coating liquid Silicone ru
Basic Info
Material | Organic Silicone |
Application | Industrial |
Density | 1.07 g/cm3 |
Transport Package | 25 Kg, 200 Kg Drums, or 1000 Kg IBC Tank |
Trademark | Iota |
Origin | Anhui Bengbu |
HS Code | 39100000 |
Production Capacity | 1000tons |
Product Description
Special coating liquid silicone rubber for airbag IOTA M1740DescriptionM1740 A/B is a special coating liquid Silicone rubber for airbag with self-adhesive properties to PA66. AdvantagesExcellent self adhesion to PA66 low viscosity and easy automatic feeding Rapid heat curinglong operation time after mixingExcellent mechanical propertiesApplicationAirbag coatingArchitectural textile coatingProtective clothing coating3C product sealing, etcCuring conditionTemperature: 160°CCuring time:T90 less than 25sNoteIOTA M1740 A/B is a platinum catalyzed product. The platinum catalyst is in the component A. Strict attention should be paid when using, to avoid catalyst poisoning.Packing and storageComponent A:200kg/iron drum, component B:200kg/iron drumStorage- Below 23°C, unopened barrels can be stored for 12 months, and the best use-by date is marked on the label of each product's outer packaging.
Properties | Test method | Value |
Unmixed | ||
Component A | ||
Color | slight yellow | |
Density | 1.07 g/cm3 | |
Viscosity at 25ºC,0.9S-1 | Brookfield | 45000 mPa.s |
Component B | ||
Color | Milk white | |
Density | 1.07 g/cm3 | |
Viscosity at 25ºC,0.9S-1 | Brookfield | 53000 mPa.s |
Technical data(A+B mixed) | ||
Mix ratio(weight) | A:B | 1:1 |
Viscosity at 25ºC,0.9S-1 | Brookfield | 52000 mPa.s |
Curing time | See curing conditions | |
Technical data(cured) | 165±2ºC*300 S | |
Color | slight yellow | |
Density at 23ºC | DIN EN ISO 1183 | 1.07 g/cm3 |
Hardness | DIN ISO 48-4 | 35 |
Tensile strength | ISO 37 type 1 | 5.0 Mpa |
Elongation at break | ISO 37 type 1 | 350% |
Tear strength | ASTM D 624 B | 10 KN/m |